Here’s a whole new way to boost the flow of polycarbonate without the drawbacks of other flow modifiers. The secret is a low-molecular-weight cyclic oligomer form of PBT polyester that literally “flows like water” in molten form. This is a brand-new use of CBT (cyclic PBT) resin from Cyclics Corp., owner of patented resin technology originally developed by General Electric. Normally, CBT is used on its own for injection molding with a catalyst that causes the relatively short-chain CBT molecules to link up inside the mold, forming typical high-molecular-weight PBT engineering thermoplastic.

The idea of using CBT without catalyst as a flow modifier for other resins has been commercialized first in Korea by compounder and distributor PolymersNet Co. Ltd. of Seoul. It has a customer injection molding parts for a portable digital memory card only 0.2 mm thick. The molder is using a melt blend of CBT and PC in place of the previous high-heat ABS.

Featured Content

How Vacuum Drying Is Revolutionizing Plastics Processing READ MORE

A Purge Solution for the Blow Molding and Compounding Industries READ MORE

ColorForm From KraussMaffei Brings Key Competencies to One System READ MORE

As shown in the accompanying table, only 3% to 5% of CBT increases the melt flow of PC by 30% to 50% or more—even with 40% glass—while maintaining good mechanical properties as well as clarity. Stiffness and heat resistance are slightly reduced. According to sources at Cyclics and a major PC resin producer, other flow-enhancing additives tried with PC severely compromise its impact strength. In the case of one PC resin tested by Polymers Net, addition of 3% CBT 100 resin boosted MFR from 27 to 40.5 g/10 min while notched Izod impact strength went from 77 to 73 kgf-cm/cm2 and tensile and flexural strengths, modulus, and elongation were similarly unaffected.

Just add pellets

The CBT is mixed with PC by compounding in an extruder before molding or by feeding “salt-and-pepper” blends of PC and CBT pellets directly into the molding machine hopper. CBT melts at a moderate temperature—175-180 C or 345-355 F. Adding CBT reportedly also improves dispersion of reinforcements, pigments, and other additives.

Cyclics is working with PC manufacturers, compounders, and molders on other applications, such as cell-phone parts. The company reports early signs that CBT improves flow in acetal, PET, and nylons.